The best routes were confirmed, in which the dimensional accuracy was improved to satisfy the requirements, ensuring the mechanical properties of the product for the application demand at the same time. The dimensional accuracies and mechanical properties of fiber-reinforced polyamide products are influenced by moisture and temperature because PA66 has a high polarity and tends to absorb water molecules to form hydrogen bonds. The Western Union Company is a financial services and communications company based in the United States. The dimension and tolerance requirements of the plate are shown in Figure 1, and the thickness of the plate is 6 mm.

Annealing effect on crystalline structure and mechanical properties in long glass fibers reinforced polyamide 66. The transverse and longitudinal peripheral dimensions of the plate treated by the three routes: (a) I, (b) II, and (c) III.The dimensional accuracies and mechanical properties of the plate meet the engineering requirements, as shown in Figure 1 and Table 2, respectively.

Both the GFs and the PA66 matrix treated by route III experience brittle fracture, verifying the lower strengths and low impact strength of the dried parts.However, to improve the chemical, corrosion, mechanical, and heat resistance [ 1, 2, 3, 4], reinforcing phase, such as glass fibers (GFs), is added to the PA66 matrix to manufacture glass fiber-reinforced composites (e. Influence of water on the short and long term mechanical behaviour of polyamide 6(polyamide) fibres and yarns. Route I involved boiling water bath alone, route II involved boiling water bath after adding a “supporting mold,” and route III involved adding a “supporting mold” after boiling water bath, as shown in Figure 4. A plate used in a medium voltage switch, made by a 25 wt% glass fiber-reinforced polyamide 66 composite filled with flame-retardant red phosphorus (RP) (PA66-GF25 FR (RP)), was injection molded. First, it can be found from the high magnification SEM images ( Figure 10(d)–(f)) that a certain amount of PA66 adheres to the fibers, which indicates that the interface bonding of the composite is not reduced by water absorption [ 19, 20, 21, 22].